Using Mesoporous Carbon Electrodes for Brackish Water Desalination

Zou, Linda and Li, Lixia and Song, Huaihe and Morris, Gayle E (2008) Using Mesoporous Carbon Electrodes for Brackish Water Desalination. Water Research : a Journal of the International Water Association (IWA), 42 (8-9). pp. 2340-2348. ISSN 0043-1354

Full text for this resource is not available from the Research Repository.

Abstract

Electrosorptive deionisation is an alternative process to remove salt ions from the brackish water. The porous carbon materials are used as electrodes. When charged in low voltage electric fields, they possess a highly charged surface that induces adsorption of salt ions on the surface. This process is reversible, so the adsorbed salt ions can be desorbed and the electrode can be reused. In the study, an ordered mesoporous carbon (OMC) electrode was developed for electrosorptive desalination. The effects of pore arrangement pattern (ordered and random) and pore size distribution (mesopores and micropores) on the desalination performance was investigated by comparing OMC and activated carbon (AC). It were revealed from X-ray diffraction and N2 sorption measurements that AC has both micropores and mesopores, whereas ordered mesopores are dominant in OMC. Their performance as potential electrodes to remove salt was evaluated by cyclic voltammetry (CV) and galvanostatic charge/discharge tests at a range of electrolyte concentrations and sweep rates. It is deduced that under the same electrochemical condition the specific capacitance values of OMC electrode (i.e. 133 F/g obtained from CVat a sweep rate of 1 mV/s in 0.1M NaCl solution) are larger than those of AC electrode (107 F/g), suggesting that the former has a higher desalting capacity than the latter. Furthermore, the OMC electrode shows a better rate capacity than the AC electrode. In addition, the desalination capacities were quantified by the batch-mode experiment at low voltage of 1.2V in 25ppm NaCl solution (50 ms/cm conductivity). It was found that the adsorbed ion amounts of OMC and AC electrodes were 11.6 and 4.3 mmol/g, respectively. The excellent electrosorptive desalination performance of OMC electrode might be not only due to the suitable pore size (average of 3.3 nm) for the propagation of the salt ions, but also due to the ordered mesoporous structure that facilitates desorption of the salt. Based on the results, it was found that the development of an ordered mesoporous structure and the control of the number of micropores are two important strategies for optimising electrode material properties for electrosorptive deionisation.

Item Type: Article
Uncontrolled Keywords: ResPubID13179. mesoporous carbon electrodes, porous carbon materials, brackish water desalination, ordered mesoporous carbon, ordered mesopores, activated carbon porous, desalination, water treatment, electrosorption, electrosorptive deionisation, salt ions, sodium, cyclic voltammetry
Subjects: FOR Classification > 0399 Other Chemical Sciences
Faculty/School/Research Centre/Department > Institute for Sustainability and Innovation (ISI)
RFCD Classification > 290000 Engineering and Technology
Depositing User: VUIR
Date Deposited: 17 Aug 2011 00:08
Last Modified: 05 Mar 2014 11:26
URI: http://vuir.vu.edu.au/id/eprint/4099
ePrint Statistics: View download statistics for this item
Citations in Scopus: 97 - View on Scopus

Repository staff only

View Item View Item

Search Google Scholar